SS Plate 310H from China manufacturer - Tianjin Zhongyuanyuanda Steel Co.,Ltd.

Payment Terms:	T/T,L/C
Place of Origin:	Shanghai, China (Mainland)


	Add to My Favorites
HiSupplier Escrow	Share \|

Product Detail

Model No.: 310H

Production Capacity: 5000 tons per month

Delivery Date: About 7-15 days after we ha...

Brand:: TISCO

Surface Finish:: 2B,Ba,HL,4K,6K,8K,Mirror,No...

HS:: 7419000000

Composition:: High quality Steel

Shape:: Flat

Means of Transport: Ocean,Land,Air

Packing: Seaworthy package with wood...

Model No:: SS Plate 310H

Standard:: ASTM, AISI, IS, DIN, EN, UN...

Technique:: HR&CR

QC:: ISO

Applications:: Mineral.Metallurgy.Petroleu...

SS Plate 310H is an austenitic heat resisting alloy with excellent resistance to oxidation under mildly cyclic conditions to 2100°F.

ATTRACTIVE PRICE--SS Plate 310H--304/304L/316/316L--ba,no.1,acid

The high chromium and medium nickel contents SS Plate 310H has good resistance to hot corrosion in a variety of environments. SS Plate 310H has fair resistance to polythionic acid attack. Resistance to intergranular attack of material intended for service in the 850 to 1000°F range may be improved by thermal stabilization at 1500-1650°F for four hours. SS Plate 310H is susceptible to chloride ion stress corrosion cracking but is superior in this respect to the lower alloy stainless 304 and 316.

Specifications:

310H stainless steel plate and sheet,

Grade:200,300,400,600,900 series

Thick:0.3-100mm

Width:1000-2000mm

Surface:2B,BA,NO.1,

ASTM 310H stainless steel plate and sheet,

*******************************************************************************************************************
Description:

1) Grade: 201,202,301,304,304L,310S,316,316L,410,430,904,904Letc.

2) Standard: AISI, ASTM, DIN, GB, JIS, SUS

3) Thickness:0.3mm-100mm

4) Width:1000-2000mm

5) Production technology:hot rolled cold drawn

6) Surface finish: 2B,BA,NO.1,NO.4,NO.8,polish,mirror,brush

7) Packing: Standard export packing or according to customer's request ,

********************************************************************************************************************
Terms:

1) Loading Port: Tianjin
2) Delivery term: FOB,CFR, CIF

3) Delivery lead time: 7-15 days after received deposit.

4) Payment term:30% by T/T as deposit., balance will be paid by T/T before loading,

5) Quality assurance: ISO Certificate is supplied with shipment, third Party Inspection is acceptable.

Type#	UNS#	Mechnical Property
		Tensile Strength		Yield Strength,Bmin		Elongation 2 in,or 50	Hardness maxc
		Ksi	MPa	Ksi	MPa	Elongation 2 in,or 50	Brinell	Rockwell B
310	S31000	75	515	30	205	40	217	95
310S	S31008	75	515	30	205	40	217
310H	S31009	75	515	30	205	40	217	95

Hot Working

Most common hot work methods can be successfully performed after uniform heating to 2150 F (1177 C). Do not forge below 1800 F (982 C). Rapid cooling is required to maximize corrosion resistance.

Annealing

1900-2050 F (1038-1121 C) water quench.