SS Sheets 304L from China manufacturer - Tianjin Zhongyuanyuanda Steel Co.,Ltd.

Payment Terms:	T/T,L/C
Place of Origin:	Shanghai, China (Mainland)


	Add to My Favorites
HiSupplier Escrow	Share \|

Product Detail

Model No.: 304L

Production Capacity: 5000 Metric Tons Per Month

Delivery Date: 7~15 days after we have got...

Brand:: ASTM/AISI/DIN/JIS/EN/GB

Unit Price:: Negotiation

MOQ:: 1 ton

Certificate:: ISO:2008

Section:: Flat

Means of Transport: Ocean,Land,Air

Packing: Bundles,seaworthy wooden ca...

Model No:: SS Sheets 304L

Surface Finish:: 2B/BA/HL/HR*CR/NO.1/NO.4

Productivity:: 5000 mt/m

Composition:: High quality steel

HS:: 7219339000

Niobium -clad 304L (SS) is currently under consideration for use as a bipolar plate material in polymer electrolyte membrane fuel cell (PEMFC) stack.

Grade AiSi304L/sUs304L /// SS Sheets /// 304L*1.4306*022Cr19Ni10 Supplier

In some cases, the low carbon Alloy SS Sheets 304L may show a lower corrosion rate than the higher carbon Alloy 304. The data for formic acid, sulfamic acid, and sodium hydroxide illustrate this. Otherwise, the Alloys SS Sheets 304, SS Sheets 304L, and SS Sheets 304H may be considered to perform equally in most corrosive environments. A notable exception is in environments sufficiently corrosive to cause intergranular corrosion of welds and heat-affected zones on susceptible alloys SS Sheets 304,SS Sheets 304L.

Specifications:

Δ Grade: 304 304L

Δ Standard: AISI, EN, JIS, BS

Δ Width: 1000mm, 1219mm, 1500mm, 2000mm, as client's request.

Δ Length: 1000mm, 2438mm, 6000mm, as client's request.

Δ Thickness: 0.4-6.0mm

Δ Finish: 2B, BA HL, 8K

1) NO. 1 -After hot rolling, to do heat treatment, pickling or corresponding processing on products.

2)2D - Annealed and pickling finish, semi-matt silver-grey surface. D= Dull

3)2B - Skin passed finish, , 2D light rolling between highly polished rollers B= bright

4)BA- Bright heat treatment or bright annealed, the product are of high reflectance and gloss.

5)HL-Using appropriate abrasive to grind product continuously so as to make grinding grain in it.

6)8K-The product is continuous processed with 1000 # abrasive thus it is with high gloss and

Low and Elevated Temperature Properties
Typical short time tensile property data for low and elevated temperatures are shown below. At temperatures of 1000°F (538°C) or higher, creep and stress rupture become considerations. Typical creep and stress rupture data are also shown below.

Test Temperature		0.2% Yield Strength			Tensile Strength			Elongation
°F	°C	psi	(MPa)	psi		(MPa)	Percent in 2" or 51mm
-423	-253	100,000	690	250,000		1725	25
-320	-196	70,000	485	230,000		1585	35
-100	-79	50,000	354	150,000		1035	50
70	21	35,000	240	90,000		620	60
400	205	23,000	160	70,000		485	50
800	427	19,000	130	66,000		455	43
1200	650	15,500	105	48,000		330	34
1500	815	13,000	90	23,000		160	46